钢组 |
序 号 |
统一数 字代号 |
牌 号 |
化学成分(质量分数)(％) |
||||||||
|
C |
Si |
Mn |
Cr |
Mo |
Ni |
B |
V |
其他 |
||||
|
CrMnSi |
54 |
A24302 |
30CrMnSi |
0.27-0.34 |
0.90-1.20 |
0.80-1.10 |
0.80-1.10 |
|
|
|
|
|
|
55 |
A24303 |
30CrMnSiA |
0.28-0.34 |
0.90-1.20 |
0.80-1.10 |
0.80-1.10 |
|
|
|
|
|
|
|
56 |
A24353 |
350MnSiA |
0.32-0.39 |
1.10-1.40 |
0.80-1.10 |
1.10-1.40 |
|
|
|
|
|
|
|
CrMnMo |
57 |
A34202 |
20CrMnMo |
0.17-0.23 |
0.17-0.37 |
0.90-1.20 |
1.10-1.40 |
0.20-0.30 |
|
|
|
|
|
58 |
A34402 |
40CrMnMo |
0.37-0.45 |
0.17-0.37 |
0.90-1.20 |
0.90-1.20 |
0.20-0.30 |
|
|
|
|
|
|
CrMn-Ti |
59 |
A26202 |
20CrMnTi |
0.17-0.23 |
0.17-0.37 |
0.80-1.10 |
1.00-1.30 |
|
|
|
|
Ti 0.04-0.10 |
|
60 |
A26302 |
30CrMnTi |
0.24-0.32 |
0.17-0.37 |
0.80-1.10 |
1.00-1.30 |
|
|
|
|
Ti 0.04-0.10 |
|
|
CrNi |
61 |
A40202 |
20CrNi |
0.17-0.23 |
0.17-0.37 |
0.40-0.70 |
0.45-0.75 |
|
1.00-1.40 |
|
|
|
|
62 |
A40402 |
40CrNi |
0.37-0.44 |
0.17-0.37 |
0.50-0.80 |
0.45-0.75 |
|
1.00-1.40 |
|
|
|
|
|
63 |
A40452 |
45CRni |
0.42-0.49 |
0.17-0.37 |
0.50-0.80 |
0.45-0.75 |
|
1.00-1.40 |
|
|
|
|
|
64 |
A40502 |
50CrNi |
0.47-0.54 |
0.17-0.37 |
0.50-0.80 |
0.45-0.75 |
|
1.00-1.40 |
|
|
|
|
|
65 |
A41122 |
12CrNi2 |
0.10-0.17 |
0.17-0.37 |
0.30-0.60 |
0.60-0.90 |
|
1.50-1.90 |
|
|
|
|
|
66 |
A42122 |
12CrNi3 |
0.10-0.17 |
0.17-0.37 |
0.30-0.60 |
0.60-0.90 |
|
2.75-3.15 |
|
|
|
|
|
67 |
A42202 |
20CrNi3 |
0.17-0,24 |
0.17-0.37 |
0.30-0.60 |
0.60-0.90 |
|
2.75-3.15 |
|
|
|
|
|
68 |
A42302 |
30CrNi3 |
0.27-0.33 |
0.17-0.37 |
0.30-0.60 |
0.60-0.90 |
|
2.75-3.15 |
|
|
|
|
|
69 |
A42372 |
37CrNi3 |
0.34-0.41 |
0.17-0.37 |
0.30-0.60 |
1.20-1.60 |
|
3.00-3.50 |
|
|
|
|
|
70 |
A43122 |
12Cr2Ni4 |
0.10-0.16 |
0.17-0.37 |
0.30-0.60 |
1.25-1.65 |
|
3.25-3.65 |
|
|
|
|
|
CrNi |
71 |
A43202 |
20Cr2Ni4 |
0.17-0.23 |
0.17-0.37 |
0.30-0.60 |
1.25-1.65 |
|
3.25-3.65 |
|
|
|
|
CrNiMo |
72 |
A50202 |
20CrNiMo |
0.17-0.23 |
0.17-0.37 |
0.60-0.95 |
0.40-0.70 |
0.20-0.30 |
0.35-0.75 |
|
|
|
|
73 |
A50403 |
40CrNiMoA |
0.37-0.44 |
0.17-0.37 |
0.50-0.80 |
0.60-0.90 |
0.15-0.25 |
1.25.1.65 |
|
|
|
|
|
CrMn-NiMo |
74 |
A50183 |
18CrNiMnMoA |
0.15-0.21 |
0.17-0.37 |
1.10-1.40 |
1.00-1.30 |
0.20-0.30 |
1.00-1.30 |
|
|
|
|
CrNi-MoV |
75 |
A51453 |
45CrNiMoVA |
0.42-0.49 |
0.17-0.37 |
0.50-0.80 |
0.80-1.10 |
0.20-0.30 |
1.30-1.80 |
|
0.10-0.20 |
|
|
76 |
A52183 |
18Cr2Ni4WA |
0.13-0.19 |
0.17-0.37 |
0.30-0.60 |
1.35-1.65 |
|
4.00-4.50 |
|
|
W0.80-1.20 |
|
|
77 |
A52253 |
25Cr2Ni4WA |
0.21-0.28 |
0.17-0.37 |
0.30-0.60 |
1.35-1.65 |
|
4.00-4.50 |
|
|
W0.80-1.20 |
|
注：
1．本标准中规定带“A”字标志的牌号仅能作为高级优质钢订货，其他牌号按优质钢订货。
2．根据需方要求，可对表中各牌号按高级优质钢(指不带“A”)或特级优质钢(全部牌号)订货，只需在所订牌号后加“A”或“B”字标志(对有“A”字牌号应先去掉“A”)。需方对表中牌号化学成分提出其他要求可按特殊要求订货。
3．统一数字代号系根据GB／T 17616规定列入，优质钢尾部数字为“2”，高级优质钢(带“A”钢)尾部数字为“3”，特级优质钢(带“E”钢)尾部数字为“6”。
4．稀土成分按0.05％计算量加入，成品分析结果供参考。
5．钢中硫、磷及残余铜、铬、镍、钼含量应符合下表的规定。